Indian Journal of Science and Technology
DOI: 10.17485/ijst/2016/v9i41/100936
Year: 2016, Volume: 9, Issue: 41, Pages: 1-8
Original Article
Syed Khaja Naimuddin1*, Touseef Md2 , K. Vidhu1 , Mustafa Asim Mohamad2 and Yousuf Ali3
1Vignan University, Guntur - 522213, Andhra Pradesh, India; [email protected], [email protected] 2UCET, Acharya Nagrajuna University, Guntur - 522510, Andhra Pradesh, India; [email protected] 3NSAKCET, Hyderabad, Hyderabad - 500024, Telangana, India; [email protected]
*Author for correspondence
Syed Khaja Naimuddin Vignan University, Guntur - 522213, Andhra Pradesh, India; [email protected]
Objectives: To analyze the wear behaviour of friction stir welding on similarAA6061-AA6061, AA6082-6082 and dissimilar Alloys AA6061-6082 with T6 condition and varying track diameters. Methods/Statistical Analysis: Ultrasonic test and penetratetest are some of the Non Destructive Test methods are used to check the weld defects. Pin on disc method is used to study the wear behavior. Metallurgical microscope is used for Micro structure analysis. Analysis of sliding distance Vs. weight loss was performed for samples of welded and non welded zones of similar Alloys AA6061-AA6061, AA6082-6082 and dissimilar Alloys AA6061-6082. Findings: NDT tests have shown no deflects inwelded zone,less amount of weight loss and similar material AA6061-6061 welded joints, has better outcome in welded zone. Applications: Further corrosion test and XRD analysis can be performed as Aluminum alloys has application in marine and modern transportation.
Keywords: Friction Stir Welding, Metallurgical Microscopes, Pin-on-disc, Sliding Distance vs.Weight Loss, Wear Behavior, XDR Analysis,